A comparison of two Nextel 440 fibre reinforced aluminium composites using acoustic emission
Faculty
Not Specified
Year:
1997
Type of Publication:
Article
Pages:
3135-3142
Authors:
Sallam, HEM, Pacheco, T, NayebHashemi, H
DOI:
10.1023/A:1018642415906
Journal:
JOURNAL OF MATERIALS SCIENCE CHAPMAN HALL LTD
Volume:
32
Research Area:
Materials Science
ISSN
ISI:A1997XG48000007
Keywords :
, comparison , , Nextel , fibre reinforced aluminium composites
Abstract:
The acoustic emission (AE) response and mechanical behaviour of two Nextel 440 fibre reinforced aluminium composites were compared. The total cumulative AE events were found to occur in two regions. The first region occurred at smaller strains and had a large exponential rise in events for the reinforced 6061 composite and few events for the high purity aluminium matrix composite. The difference was attributed to the alloy constituents of the 6061 aluminium matrix. The events were attributed to a dislocation release mechanism that occurred prior to yielding of the matrix. In the second region of events in the reinforced 6061 composite the event rate was constant and continued to failure. The second region of events in the high purity aluminium (HPAL) composite had a steady increase in the event rate until a constant rate was reached prior to failure. The events in the reinforced HPAL composite were attributed to the fracturing of fibres and the associated plastic deformation of the matrix that accompanies fibre failure. Thus failure in the materials occurs due to the propagation of fracturing fibres. The propagation was rapid in the reinforced 6061 aluminium composite. The reinforced HPAL composite had a slower propagation due to the high ductility of the HPAL.
Online
PDF
جامعة المنصورة
جامعة الاسكندرية
جامعة القاهرة
جامعة سوهاج
جامعة الفيوم
جامعة بنها
جامعة دمياط
جامعة بورسعيد
جامعة حلوان
جامعة السويس
شراقوة
جامعة المنيا
جامعة دمنهور
جامعة المنوفية
جامعة أسوان
جامعة جنوب الوادى
جامعة قناة السويس
جامعة عين شمس
جامعة أسيوط
جامعة كفر الشيخ
جامعة السادات
جامعة طنطا
جامعة بنى سويف