Dissolution susceptibility of the oxide species formed on mild steel during its oxidation in molten NaNO3-KNO3 eutectic mixture
Faculty
Science
Year:
2002
Type of Publication:
Article
Pages:
301-305
Authors:
Attia, AA, Baraka, AM, Abdel-Hakim, HA
DOI:
10.1361/105994902770344114
Journal:
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE ASM INTERNATIONAL
Volume:
11
Research Area:
Materials Science
ISSN
ISI:000176503600012
Keywords :
dissolution in sulfuric acid, mild steel, NaNO3-KNO3 eutectic, oxidation
Abstract:
Mild steel was oxidized in pure molten NaNO3-KNO3 eutectic mixture at temperatures of 300, 375, and 450 degreesC and in the presence of 0.05 molal KH2PO4, K2Cr2O7, or Na2O2 as additives. The dissolution susceptibility of the formed oxide species was evaluated in H2SO4 acid solution using the potential-time and current-time measurements under the open-circuit conditions. It was found that the rate of dissolution depended on the composition of molten nitrate bath, used for oxidation of mild steel, and its temperature. This was attributed to the effect of the previous conditions of the nitrate bath on the nature and composition of the oxide species formed on the metallic surface. The more resistant to dissolution in H2SO4 solution were those electrodes that were oxidized in nitrate melt at 450 degreesC in the presence of K2Cr2O7 or Na2O2 as additives.
Online
PDF
جامعة المنصورة
جامعة الاسكندرية
جامعة القاهرة
جامعة سوهاج
جامعة الفيوم
جامعة بنها
جامعة دمياط
جامعة بورسعيد
جامعة حلوان
جامعة السويس
شراقوة
جامعة المنيا
جامعة دمنهور
جامعة المنوفية
جامعة أسوان
جامعة جنوب الوادى
جامعة قناة السويس
جامعة عين شمس
جامعة أسيوط
جامعة كفر الشيخ
جامعة السادات
جامعة طنطا
جامعة بنى سويف