Effect of isothermal ageing on the electrical resistivity and microstructure of Pb-Sn-Zn ternary alloys
Faculty
Science
Year:
2003
Type of Publication:
Article
Pages:
73-80
Authors:
Abdel-Daiem, AM, El-Daly, AA, Yousf, M
DOI:
10.1016/S0254-0584(02)00309-7
Journal:
MATERIALS CHEMISTRY AND PHYSICS ELSEVIER SCIENCE SA
Volume:
78
Research Area:
Materials Science
ISSN
ISI:000179262700014
Keywords :
isothermal ageing, electrical resistivity, ternary alloys
Abstract:
Electrical resistivity measurements (Deltarho/rho(0)) Were carried out on (Pb-65.5Sn-3.4Zn) eutectic and (Pb-65Sn-1.0Zn) ternary alloys, at various ageing temperatures for various ageing times. Both alloys showed enhancement in the reaction rate in comparison to those of binary eutectic Pb-Sn alloy, the variations of microstructure with ageing temperature were investigated by transmission electron microscope (TEM), X-ray, microhardness, and differential thermal analysis (DTA). It was concluded that the Pb-Sn-Zn ternary alloys show progressive reduction in the electrical resistivity compared with the Pb-Sn binary eutectic composition as a result of the nature of the internal stresses induced by the Zn particles and the multiplicity of types of interphase boundary causing enhancement in the driving force for the coarsening process. (C) 2002 Elsevier Science B.V. All rights reserved.
Online
PDF
جامعة المنصورة
جامعة الاسكندرية
جامعة القاهرة
جامعة سوهاج
جامعة الفيوم
جامعة بنها
جامعة دمياط
جامعة بورسعيد
جامعة حلوان
جامعة السويس
شراقوة
جامعة المنيا
جامعة دمنهور
جامعة المنوفية
جامعة أسوان
جامعة جنوب الوادى
جامعة قناة السويس
جامعة عين شمس
جامعة أسيوط
جامعة كفر الشيخ
جامعة السادات
جامعة طنطا
جامعة بنى سويف