Thermal and optical properties of electron beam irradiated cellulose triacetate
Faculty
Science
Year:
2009
Type of Publication:
Article
Pages:
813-819
Authors:
Nouh, S. A, Mohamed, Amal, El Hussieny, H. M
Journal:
INDIAN JOURNAL OF PHYSICS AND PROCEEDINGS OF THE INDIAN ASSOCIATION FOR THE CULTIVATION OF SCIENCE INDIAN ASSOC CULTIVATION SCIENCE
Volume:
83
Research Area:
Physics
ISSN
ISI:000267872600009
Keywords :
Electron beam irradiation, thermal properties, color response, polymers
Abstract:
Samples from Cellulose triacetate (CTA) sheets were irradiated with electron beam in the dose range 10-200 kGy. Non-isothermal studies were carried out using thermogravimetric analysis (TGA) to obtain the activation energy of thermal decomposition for CTA polymer. The CTA samples decompose in one main break down stage. The results indicate that the irradiation by electron beam in the dose range 80-200 kGy increases the thermal stability of the polymer samples. Also, the variation of melting temperatures with the electron dose has been determined using differential thermal analysis (DTA). The CTA polymer is characterized by the appearance of one endothermic peak due to melting. It is found that the irradiation in the dose range 10-80 kGy causes defects generation that splits the crystals depressing the melting temperature, while at higher doses (80-200 kGy), the thickness of crystalline structure (lamellae) is increased, thus the melting temperature increases. In addition, the transmission of these samples in the wavelength range 200-2500 nm, as well as any color changes, were studied. The color intensity 60 was greatly increased on increasing the electron beam dose, and accompanied by a significant increase in the blue color component.
Online
PDF
جامعة المنصورة
جامعة الاسكندرية
جامعة القاهرة
جامعة سوهاج
جامعة الفيوم
جامعة بنها
جامعة دمياط
جامعة بورسعيد
جامعة حلوان
جامعة السويس
شراقوة
جامعة المنيا
جامعة دمنهور
جامعة المنوفية
جامعة أسوان
جامعة جنوب الوادى
جامعة قناة السويس
جامعة عين شمس
جامعة أسيوط
جامعة كفر الشيخ
جامعة السادات
جامعة طنطا
جامعة بنى سويف