Some magnetic properties of Li-Ga ferrite in low magnetic field
Faculty
Science
Year:
2009
Type of Publication:
Article
Pages:
51-58
Authors:
Mansour, S. F, Zaki, H. M, Elmosalami, T. A, Dhahri, E, Mazen, S. A
DOI:
10.1016/j.matchemphys.2009.04.026
Journal:
MATERIALS CHEMISTRY AND PHYSICS ELSEVIER SCIENCE SA
Volume:
117
Research Area:
Materials Science
ISSN
ISI:000269291500012
Keywords :
Li-Ga ferrite, X-ray, Magnetization, B-H loop
Abstract:
Li-gallium ferrites with the chemical formula Li(0.5)Ga(x)Fe(2.5-x)O(4) (x = 0, 0.1, 0.2. 0.3, 0.4 and 0.5) have been prepared by the ceramic method technique. The spinel structure in homogenous state was realized by X-ray diffraction analysis. The lattice parameter was determined for each composition and it was found approximately constant value (0.832 nm). Some magnetic properties such as magnetization M, and (B-H) loop were measured at room temperature. The magnetization M was measured in the range of magnetizing field up to 800 A m(-1). The B-H loops were measured at elevated temperature and magnetizing current (I = 1A which is equivalent to 200 A m(-1)). At room temperature the relative permeability (mu(r)) was calculated from M-H relation. Also, remanence magnetization (M(r)), saturation magnetization (M(s)) and apparent loss energy (P(s)) were estimated from B-H loops. It was found that mu(r), M(r), M(s) and P(s) are composition dependent. The initial permeability (mu(i)) was measured as a function of temperature from room temperature up to 893 K. The Curie temperature T(c) and paramagnetic temperatures (T(p) and T(s))were determined. These values of temperature have been found to decrease with increasing Ga(3+) content. (C) 2009 Published by Elsevier B.V.
Online
PDF
جامعة المنصورة
جامعة الاسكندرية
جامعة القاهرة
جامعة سوهاج
جامعة الفيوم
جامعة بنها
جامعة دمياط
جامعة بورسعيد
جامعة حلوان
جامعة السويس
شراقوة
جامعة المنيا
جامعة دمنهور
جامعة المنوفية
جامعة أسوان
جامعة جنوب الوادى
جامعة قناة السويس
جامعة عين شمس
جامعة أسيوط
جامعة كفر الشيخ
جامعة السادات
جامعة طنطا
جامعة بنى سويف