Influence of Calcium Ions on the Structural and Magnetic Properties of Cd-Mg Ferrites Nanoparticles
Faculty
Science
Year:
2012
Type of Publication:
Article
Pages:
7126-7131
Authors:
Zaki, H. M, Al-Heniti, S
DOI:
10.1166/jnn.2012.6586
Journal:
JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY AMER SCIENTIFIC PUBLISHERS
Volume:
12
Research Area:
Chemistry; Science \& Technology - Other Topics; Materials Science; Physics
ISSN
ISI:000308856200036
Keywords :
Ferrites, Nano-Particles, Co-Precipitation, Magnetization, Cation Distribution
Abstract:
Cadmium magnesium ferrites doped with calcium having the chemical formula Cd0.5Mg0.5-x CaxFe2O4 (0.0 <= x <= 0.3) were prepared by the Co-precipitation method. X-ray diffraction analysis confirmed the formation of a single phase with spinel crystal structure for the samples. The lattice parameter is determined for each composition and has been found to increase from 8.505 angstrom to 8.626 angstrom with increasing calcium concentration. Cation distribution for the studied ferrite system is proposed in terms of the structural and magnetic properties by means of X-ray diffraction (XRD), infrared spectroscopy (IR), vibrating sample magnetometer (VSM) and is found to be reliable. The experimental and theoretical lattice constants show the same trend with increasing calcium concentration indicating the validity of the proposed cation distribution. The analysis of infrared spectra indicates the presence of splitting in the absorption band which may be attributed to the presence of small amounts of Fe2+ ions in the ferrite system. The appearance of a shoulder around 700 cm(-1) suggests the presence of calcium ions in the tetrahedral site. The addition of non magnetic calcium ions in the ferrites suppressed the A-interaction and developed a B B interaction, which is reflected in reducing the saturation magnetization in the present samples. The coercive field (H-c) is also found to increase by increasing of Ca2+ concentration and has been explained on the bases of direct relationship with anisotropy constant.
Online
PDF
جامعة المنصورة
جامعة الاسكندرية
جامعة القاهرة
جامعة سوهاج
جامعة الفيوم
جامعة بنها
جامعة دمياط
جامعة بورسعيد
جامعة حلوان
جامعة السويس
شراقوة
جامعة المنيا
جامعة دمنهور
جامعة المنوفية
جامعة أسوان
جامعة جنوب الوادى
جامعة قناة السويس
جامعة عين شمس
جامعة أسيوط
جامعة كفر الشيخ
جامعة السادات
جامعة طنطا
جامعة بنى سويف